Pengaruh Serat Ban Bekas dan Abu Batu Bara Terhadap Kuat Tarik Beton

Bunyamin Bunyamin, Imransyah Idroes, Reska Wahyu Fauzha

Abstract


In today's modern era, technological developments are needed to increase development in all fields. The manufacture of concrete can use partial cement substitution materials through the use of industrial by-products such as fly ash and fiber waste from used tires. The benefit of this research is to develop knowledge about concrete technology. The method used in this research is the ACI 211.1-91 (American Concrete Institute) and ASTM (American Society for Testing and Materials) methods with variations in the addition of used tire fiber by 0%, 5%, 10%, 15%, and 5% addition of fly ash from the weight of cement in each variation. The test object used is a cylinder with dimensions of 15 cm x 30 cm with a total of 20 test objects, the planned concrete quality is 17.00 MPa. The tensile strength of concrete test was carried out at the age of 28 days. The results of this study are that concrete with a variation of 0% produces a tensile strength of 2.32 MPa; while the tensile strength with variations of 5%, 10% and 15% were 2.71 MPa, 2.50 MPa and 2.41 MPa. The tensile strength of concrete using tire fiber waste and fly ash increases compared to normal concrete.


Full Text:

PDF

References


M. S. Imbabi, C. Carrigan, and S. McKenna, “Trends and developments in green cement and concrete technology,” Int. J. Sustain. Built Environ., vol. 1, no. 2, pp. 194–216, 2012.

C. Wang, C. Yang, F. Liu, C. Wan, and X. Pu, “Preparation of Ultra-High Performance Concrete with common technology and materials,” Cem. Concr. Compos., 2012, doi: 10.1016/j.cemconcomp.2011.11.005.

D. Permukiman and P. Wilayah, “Tata Cara Pembuatan dan Pelaksanaan Beton Berkekuatan Tinggi (PD T-04-2004-C),” Dep. Pekerj. Umum, 2004.

M. Hasan, T. Saidi, M. Jamil, and M. F. Fadillah, “The resistance of high strength concrete with diatomaceous earth exposed to high temperatures,” in AIP Conference Proceedings, 2023, vol. 2613, no. 1, p. 30002.

M. Hasan, M. Jamil, and T. Saidi, “Mechanical properties and durability of ultra-high-performance concrete with calcined diatomaceous earth as cement replacement,” J. Mech. Behav. Mater., vol. 32, no. 1, p. 20220272, 2023.

D.-Y. Yoo and N. Banthia, “Mechanical properties of ultra-high-performance fiber-reinforced concrete: A review,” Cem. Concr. Compos., vol. 73, pp. 267–280, 2016.

Y. Ding, G. Liu, A. Hussain, F. Pacheco-Torgal, and Y. Zhang, “Effect of steel fiber and carbon black on the self-sensing ability of concrete cracks under bending,” Constr. Build. Mater., vol. 207, pp. 630–639, 2019.

J. Di Filippo, J. Karpman, and J. R. DeShazo, “The impacts of policies to reduce CO2 emissions within the concrete supply chain,” Cem. Concr. Compos., vol. 101, pp. 67–82, 2019.

N. C. Onyenokporo, “Supplementary Cementitious Materials as Sustainable Partial Replacement for Cement in the Building Industry,” Int. J. Archit. Environ. Eng., vol. 16, no. 3, pp. 74–84, 2022.

S. Fernando, C. Gunasekara, D. W. Law, M. C. M. Nasvi, S. Setunge, and R. Dissanayake, “Life cycle assessment and cost analysis of fly ash--rice husk ash blended alkali-activated concrete,” J. Environ. Manage., vol. 295, p. 113140, 2021.

W. Wu, R. Wang, C. Zhu, and Q. Meng, “The effect of fly ash and silica fume on mechanical properties and durability of coral aggregate concrete,” Constr. Build. Mater., vol. 185, pp. 69–78, 2018.

H. Wardhana and N. H. Haryanti, “Studi abu dasar batubara sebagai bahan konstruksi campuran beton,” INFO-TEKNIK, vol. 2, no. 1, pp. 39–41, 2001.

D. Siang et al., “Influence of SiO2, TiO2 and Fe2O3 nanoparticles on the properties of fly ash blended cement mortars,” Constr. Build. Mater., vol. 258, 2020, doi: 10.1016/j.conbuildmat.2020.119627.

Z. Abidin, B. Bunyamin, and F. D. Kurniasarir, “Uji Marshall Pada Campuran AC-WC Dengan Substitusi Filler,” J. Serambi Eng., vol. 6, no. 1, 2021.

F. D. Pratama, B. Bunyamin, and F. D. Kurniasari, “PENGARUH PENGGUNAAN SUBTITUSI FILLER SERBUK KAYU PADA CAMPURAN LAPISAN ASPAL BETON,” J. Tek. Sipil Unaya, vol. 7, no. 2, pp. 123–134, 2021.

A. Amiruddin, F. D. Kurniasari, and B. Bunyamin, “PENGARUH SUBSTITUSI STYROFOAM PADA ASPAL DENGAN METODE PENCAMPURAN KERING LASTON ASPHALT CONCRETE-WEARING COURSE (AC-WC),” J. Tek. Sipil dan Teknol. Konstr., vol. 7, no. 1, 2021.

F. Kurniasari, B. Bunyamin, A. Amin, and others, “Pemanfaatan Abu Cangkang Sawit (ACS) Untuk Subtitusi Filler Pada Asphalt Concrete Wearing Course,” J. Tek. Sipil Unaya, vol. 8, no. 2, pp. 204–214, 2022.

M. I. M Irpan, “PENGARUH PENAMBAHAN HANCURAN KARET (CRUMB RUBBER) PADA CAMPURAN BETON TERHADAP SIFAT MEKANIK BETON,” Universitas Mataram, 2017.

M. Muhajir, I. Idroes, and B. Bunyamin, “KONTRIBUSI SERAT LIMBAH BAN BEKAS KENDARAAN TERHADAP KUAT TARIK BELAH BETON,” J. Tek. Sipil dan Teknol. Konstr., vol. 8, no. 1, 2022.

M. Hady, B. Bunyamin, D. Darwin, A. Rahman, and A. Satria, “Pemanfaatan Cangkang Keong Sawah Sebagai Substitusi Sebahagian Semen Dan Agregat Halus Terhadap Kuat Tekan Beton,” J. Tek. Sipil dan Teknol. Konstr., vol. 8, no. 1, 2022.

B. S. Nasional, “Persyaratan Beton Struktural untuk Bangunan Gedung dan Penjelasan (SNI 2847: 2019).” Jakarta, 2019.

B. Bunyamin and A. Mukhlis, “Utilization of Oyster Shells as a Substitute Part of Cement and Fine Aggregate in the Compressive Strength of Concrete,” Aceh Int. J. Sci. Technol., vol. 9, no. 3, 2020.

B. Bunyamin, F. D. Kurniasari, R. P. Munirwan, and R. Putra Jaya, “Effect of Coral Aggregates of Blended Cement Concrete Subjected to Different Water Immersion Condition,” Adv. Civ. Eng., vol. 2022, 2022.

A. C33/C33M-13, “Standard Specificationfor Concrete Aggregates,” A.S.T.M. Int. WestConshohocken P.A. vol. 04.02 p. 11, 2013.

B. Bunyamin, R. P. Munirwan, M. Ridha, and N. Hendrifa, “Utilization of wood processing dust as a substitute for a part of cement in concrete,” in IOP Conference Series: Materials Science and Engineering, 2021, vol. 1087, no. 1, p. 12004.

D. ASTM, “ASTM D-2240,” 2015.

A. C. I. C. 211, “Standard Practice for Selecting Proportions for Normal, Heavyweight, and Mass Concrete:(ACI 211.1-91),” 1991.

B. Bunyamin, N. Hendrifa, and M. Ridha, “PENGARUH SUBSTITUSI CANGKANG TIRAM SEBAGAI PENGGANTI SEBAHAGIAN SEMEN DAN PASIR HALUS TERHADAP KUAT TARIK BELAH BETON,” TERAS J., vol. 11, no. 2, pp. 272–281, 2021.

A. C496/C496M-11, “Standard Test Methodfor Splitting Tensile Strength for CylindricalConcrete Specimens,” A.S.T.M. Int. WestConshohocken P.A. vol. 04.02 p. 5, 2011.




DOI: https://doi.org/10.35308/jts-utu.v9i1.7092

Refbacks

  • There are currently no refbacks.


Copyright (c) 2023 Jurnal Teknik Sipil dan Teknologi Konstruksi